Analysis of Variation E7016 Electrode Heating Time and Humidity on E7016 Electrode Tensile Strength of Joints Welding Material SS400
DOI:
https://doi.org/10.53893/ijmeas.v2i3.305Keywords:
E7016 Electrode, Heating Time, Electrode Humidity, SS400Abstract
This research aims to determine the effect of variations in heating time and humidity of the E7016 electrode on the tensile strength of welded joints in SS400 material. The research was carried out using three humidity levels and two electrode heating durations (2 hours and 3 hours) at a temperature of 260°C. The research results show that electrode humidity and heating time have a significant influence on the tensile strength of the welded joint. The highest tensile strength value was found in the welding variation using welding wire without treatment with heating for 3 hours with an average of 529.62 N/mm2, then the lowest tensile stress was found in the outdoor electrode humidity treatment variation with a heating time of 2 hours amounting to 378.12 N/mm2. The analysis was carried out using the two ways ANOVA method to analyze the resulting tensile strength data. The analysis results show that electrodes heated for 3 hours produce higher tensile strength compared to electrodes heated for 2 hours
Downloads
References
Putri, f. (2010). Analysis of the effect of variations in current strength and welding distance on the tensile strength of low carbon steel welded joints with 6013 electrodes. Austenit, 2(02). 16 -17
Muttaqiin, r., jufriadi, j., & rosedi, m. (2022). Analysis of variations in electrode heating temperature to reduce porosity defects with SMAW welding (case study in the Peusangan 1 & 2 hydropower project). Journal of applied science engineering, 6(1), 39-45 http://dx.doi.org/10.30811/jmst.v6i1.2857
Hafni, h., & Novriwan, n. (2023). Effect of electrode moisture in dc current SMAW process on the welding results of low carbon steel. Journal of mechanical engineering, 13(1), 27-31. https://doi.org/10.21063/jtm.2023.v13.i1.27-31
Aljufri, A., & Putra, R. (2018). The influence of weld porosity on the tensile strength of AISI 1050 material using V 90 welding joint. Proceedings of Semnastek page-6
Irawan, Y. S., Oerbandono, T., Aristiyono, D. F. A., & Pratikto, P. (2013). Tensile Strength and Porosity of Al-Mg-Si Cylinders from Die Casting with Pressure Variations. Journal of Mechanical Engineering, 4(1), 11-16 https://doi.org/10.21776/jrm.v4i1.172
Setyawan, c. W. (2019). The influence of drying temperature of e7018 electrode on the hardness value and porosity parameters on the SMAW of a36 steel. Kne social sciences, 241-246 DOI:10.18502/KSS.V3I12.4089
Afan, m. B., Purwantono, p., Mulianti, M., & Rahim, b. (2020). The effect of low hydrogen e7016 electrode storage temperature on the bending test results of SS400 carbon steel plate welded joints. Journal of mechanical engineering, 15(1), 20-25 https://doi.org/10.30811/jrm.v15i1.870 (Jurnal Polines) (Jurnal Polines)
Sudiyanto, a., mirahati, r. Z., & rahma, n. A. (2022). Pengaruh drying elektroda low hydrogen pada longitudinal weld penstock material baja sm 400 b terhadap cacat las dengan inspeksi non destructive test metode radiografi. Journal of metallurgical engineering and processing technology, 2(2), 123-129
Julian, N. (2019). Comparative Analysis of Tensile Strength in MAG Welded SS400 Steel Welded Joints with Varying Welding Current and Cooling Media as Ship Hull Material. Journal of Naval Engineering, 7(4).
Rachmadi Rizki, R. D., Pranatal, E., & Imawan, P. (2022, March). Analysis of the Effect of Fairing Method on Mechanical Properties in the Welding Area of the Ship Hull. In Proceedings of SENASTITAN: National Seminar on Sustainable Industrial Technology (Vol. 2, pp. 192-199).
Azwinur, & Muhazir. (2019). The effect of SMAW welding electrode type on the mechanical properties of SS400 material. Polimesin Journal, 17(1), 19–25. https://doi.org/10.30811/jpl.v17i1.870
Damai, r., rijanto, a., & judge, l. (2022). Analysis of the effect of cooling media in SMAW welding on the tensile strength of low carbon steel Aisi 1020 steel plate. Majamecha, 4(1), 51-59.https://doi.org/10.36815/majamecha.v4i1.1321
Alsayed, A. A. (2021). Physics of Open Fractures: Reconsidering Tissue Viability, Contamination Risk and Importance of Wound Debridement. Journal of Applied Mathematics and Physics, 9(1), 176-182. https://doi.org/10.4236/jamp.2021.91012
Setiawan, FW (2021). Mechanical Properties Analysis of Tensile Testing Metal Alloy Brass 60/40 (Cu Zn), 0.4% Carbon Steel (Oil Quench-Temper) and Aluminum Bronze. JMIO: Journal of Industrial and Automotive Machinery, 2(02), 33-41.
ASTM International. (2013). Standard test methods for tension testing of metallic materials (ASTM E8/E8M − 13a). American Association of State Highway and Transportation Officials. https://www.astm.org/Standards/E8.htm
American Society of Mechanical Engineers. (2023). BPVC Section II, Materials, Part C, Specifications for Welding Rods, Electrodes, and Filler Metals. Retrieved from https://webstore.ansi.org/standards/asme/bpvciic2023
Rachmawati, DI, Yuniarti, D., & Nohe, DA (2015). Variable Regression Model with Absolute Difference Method Exponential Journal, 6(2), 187-192.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 Authors and Publisher
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.